Isotope effect for transport and magnetic properties of La 0.35 Pr 0.35 Ca 0.3 MnO 3 thin films

The effect of ¹⁶ O → ¹⁸ O isotope substitution on electrical resistivity, magnetoresistance, and ac magnetic susceptibility was studied for La_0.35Pr_0.35Ca_0.3MnO₃ epitaxial thin films deposited onto LaAlO₃ and SrTiO₃ substrates. For the films on LaAlO₃, the isotope substitution resulted in the reversible transition from a metal-like to insulating state. The applied magnetic field ( H ≥ 2 T) transformed the sample with ¹⁸O back to the metallic state. The films on SrTiO₃ remained metallic at low temperatures for both ¹⁶O and ¹⁸O, but the shift of the resistivity peak corresponding to onset of metallic state exceeded 63 K after ¹⁶ O → ¹⁸ O substitution. The temperature dependence of both resistivity and magnetic susceptibility was characterized by hysteresis, especially pronounced in the case of the films on LaAlO₃. Such a behavior gives certain indications of the phase separation characteristic of interplay between ferromagnetism and charge ordering. Received 11 February 2000 and Received in final form 13 September 2000     

具有特大磁电阻效应钙钛矿材料的制备及性能分析

通过固相烧结法制备了具有特大磁电阻效应的钙钛矿材料Pr0.64Ag0.044MnAl0.2O3.利用结构和成分分析,发现此材料只有在1 100℃高温烧结下才能生成完整的钙钛矿结构,且属于立方晶系,晶格常量a≈0.386 nm.在0.4 T的外磁场下,磁电阻值在122 K处达到最大,约为19.2%,为巨磁电阻实验提供了较好的样品.     

Charge ordering characteristics in Y0.5Ca0.5MnO3 manganite

The charge ordering characteristics in Y_0.5Ca_0.5MnO₃ manganite, prepared by sol–gel process, have been investigated experimentally. It is found that the superlattice diffractions appear in the electron diffraction patterns recorded at low temperatures, while only basic Brag diffraction spots can be observed when temperature is higher than 300 K. This provides direct evidence for the existence of charge ordering in Y_0.5Ca_0.5MnO₃. The magnetization and specific heat measurements indicate the charge ordering temperature of Y_0.5Ca_0.5MnO₃ is 290 K, around which both the magnetization and specific heat reveal anomalous behaviors. We also observed that the MnO bond length changed remarkably and the effective number of carriers reduced prominently with decreasing temperature around charge ordering temperature through transform infrared spectra measurements.     

La1/8Ca7/8MnO3/Sr0.95Nb0.05TiO3异质结的整流特性和磁输运性质

在5%Nb掺杂的SrTiO3衬底上用磁控溅射法外延生长了La1/aCa7/aMnO3薄膜形成异质结,该异质结有类似于传统P-n结的整流特性.磁场下扩散电压减小,当温度低于130 K以下,扩散电压的减小非常明显.这和在此温度以下,La1/8Ca7/aMnO3出现自旋倾斜态密切相关.我们计算出异质结的结电阻和磁致电阻(MR),在不同大小的正负偏压,不同磁场下,都得到负的MR值.我们给出界面附近的La1/8Ca7/8MnO3的能带结构并分析了外加磁场对洪德耦合,Jahn-Teller畸变等机制的作用,来解释该异质结的磁输运行为.结果有助于了解高Ca掺杂锰氧化物异质结的性质.     

大学物理铁磁质教学中工程教育素材的融入

在大学物理课程铁磁质知识点的教学中,结合工程实践教育,使讲授的知识点能够理论联系实际,在提高教学效果的同时,使学生认识到理论知识在工程实践中的应用,进而使学生树立正确的知识价值观,提高学习兴趣,增强主动学习的意识.     

La2/3Ca1/3MnO3样品的磁和电子输运性质研究

实验研究了La2/3CamMnO3样品零磁场下的电阻率和低磁场下的磁化强度随温度的变化行为．结果表明，除了居里温度(Tc)外还存在另一特征温度Tonset，高于Tonset的样品为典型的顺磁绝缘体，而低于Tc的样品为典型的铁磁金属，但在Lonset和Tc之间，样品的磁化率大大偏离居里一外斯定律，同时其导电特性显示出明显的反常．对观察到的不寻常导电特性，根据铁磁金属集团在顺磁绝缘体背景上随机分布的假设，进行了分析与探讨。     

Anomalous anisotropic magnetoresistance in single-crystalline Co/SrTiO3(001) heterostructures

The anisotropic magnetoresistances (AMRs) in single crystalline Co(6 nm)/SrTiO₃(001) heterostructures from 5 K to 300 K with the current direction setting along either Co[100] or Co[110] are investigated in this work. The anomalous (normal) AMR is observed below (above) 100 K. With the current along Co[100] direction, the AMR shows negative longitudinal and positive transverse magnetoresistances at T< 100 K, while the AMR is inverse with the current along Co[110]. Meanwhile, the amplitude ratio between Co[110] and Co[100] is observed to be as large as 29 at 100 K. A crystal symmetry-adapted model of AMR demonstrates that interplay between the non-crystalline component and crossed AMR component results in the anomalous AMR. Our results may reveal more intriguing magneto-transport behaviors of film on SrTiO₃ or other perovskite oxides.     

垂直各向异性Ho3Fe5O12薄膜的外延生长与其异质结构的自旋输运

垂直磁各向异性稀土-铁-石榴石纳米薄膜在自旋电子学中具有重要应用前景.本文使用溅射方法在(111)取向掺杂钇钪的钆镓石榴石(Gd_0.63Y_2.37Sc₂Ga₃O₁₂,GYSGG)单晶衬底上外延生长了2—100 nm厚的钬铁石榴石(Ho₃Fe₅O₁₂,HoIG)薄膜,并进一步在HoIG上沉积了3 nm Pt薄膜.测量了室温下HoIG的磁各向异性和HoIG/Pt异质结构的自旋相关输运性质.结果显示,厚度薄至2 nm的HoIG薄膜(小于2个单胞层)在室温仍具有铁磁性,且由于外延应变,2—60 nm厚HoIG薄膜都具有很强的垂直磁各向异性,有效垂直各向异性场最大达350 mT;异质结构样品表现出非常可观的反常霍尔效应和“自旋霍尔/各向异性”磁电阻效应,前者在HoIG厚度小于4 nm时开始缓慢下降,而后者当HoIG厚度小于7 nm时急剧减小,说明相较于反常霍尔效应,磁电阻效应对HoIG的体磁性相对更加敏感;此外,自旋相关热电压随HoIG厚度减薄在整个厚度范围以指数方式下降,说明遵从热激化磁振子运动规律的自旋塞贝克效应是其主要贡献者.本文结果表明HoIG纳米薄膜具有可调控的垂直磁各向异性,厚度大于4 nm的HoIG/Pt异质结构具有高效的自旋界面交换作用,是自旋电子学应用发展的一个重要候选材料.     

EuS/Ta异质结的极大磁电阻效应

在铁磁/超导异质结中,铁磁体的交换场通过近邻效应将导致超导体准粒子态密度的塞曼劈裂.基于该效应,在外磁场不强的情况下,通过外加磁场可以有效地调节铁磁/超导界面处的交换作用,从而实现超导体在正常态和超导态之间转换,产生极大磁电阻.本文利用脉冲激光沉积方法制备了EuS/Ta异质结并研究了其电磁特性.Ta在3.6 K以下为超导态,EuS在20 K以下为铁磁态.在2 K时,EuS/Ta异质结中可观测蝴蝶型磁滞回线,证明在低磁场下(<±0.18 T)异质结中EuS铁磁态和Ta超导态共存.磁输运测试表明,通过施加外磁场可以有效调节EuS的交换场,随着交换场的增大,同时也加强了界面处的交换作用,从而抑制Ta的超导态,实现了Ta在超导态和正常态之间的转变,在EuS/Ta异质结中观测到了高达144000%的磁电阻.本文制备的EuS/Ta异质结具有极大磁电阻效应,在自旋电子学器件中有潜在的应用前景.     

Transport properties and magnetoresistance in La0.8Te0.2MnO3/ZrO2 composites

The transport properties and magnetoresistance of electron-doped manganate / insulator composites (La_0.8Te_0.2MnO₃)_{1 - x}/(ZrO₂)_x (x=0, 0.3, and 0.5) are investigated. It is found that the metal-insulator transition temperature of this system shifts to a lower value as the ZrO₂ content increases. The introduction of ZrO₂ enhances both the domain scattering and electron relative scattering in the metal transport region. In the adiabatic small polaron hopping transport region, the thermal activation energy seems invariable regardless of the ZrO₂ content. The application of a magnetic field promotes the charge transportation capabilities of the composites, and the magnetoresistance is enhanced with an increase of the ZrO₂ content. This could be attributed to the more remarkable modification effect of magnetic field on ordering degree in the composites than in pure La_0.8Te_0.2MnO₃.